App/Resource/WorkpieceMaterial/17-4PH.WorkpieceMaterial
+15
View File
@@ -0,0 +1,15 @@
<?xml version="1.0" encoding="utf-8"?>
<WorkpieceMaterial>
<Name>17-4PH</Name>
<Note>chatGPT review by mei</Note>
<ElasticModulus_GPa>200</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>1100</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>1000</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.12</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.46</HeatCapacity_JdgK>
<HeatConductivity_WdmK>18</HeatConductivity_WdmK>
<Density_gdcm3>7.8</Density_gdcm3>
<PoissonRatio>0.27</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1400</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/A380.WorkpieceMaterial
+15
View File
@@ -0,0 +1,15 @@
<?xml version="1.0" encoding="utf-8"?>
<WorkpieceMaterial>
<Name>A380</Name>
<Note></Note>
<ElasticModulus_GPa>71</ElasticModulus_GPa>
<PoissonRatio>0.33</PoissonRatio>
<CompressiveYieldStrength_MPa>280</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>165</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.03</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.963</HeatCapacity_JdgK>
<HeatConductivity_WdmK>96</HeatConductivity_WdmK>
<Density_gdcm3>2.76</Density_gdcm3>
<FusionLatentHeat_Jdg>390</FusionLatentHeat_Jdg>
<MeltingTemperature_C>540</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/A6082.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>A6082</Name>
<ElasticModulus_GPa>70</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>250</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>260</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.12</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.896</HeatCapacity_JdgK>
<HeatConductivity_WdmK>180</HeatConductivity_WdmK>
<Density_gdcm3>2.7</Density_gdcm3>
<PoissonRatio>0.33</PoissonRatio>
<FusionLatentHeat_Jdg>390</FusionLatentHeat_Jdg>
<MeltingTemperature_C>555</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/AA7075.WorkpieceMaterial
+14
View File
@@ -0,0 +1,14 @@
<WorkpieceMaterial>
<Name>AA7075</Name>
<Note>AA7075</Note>
<ElasticModulus_GPa>71.7</ElasticModulus_GPa>
<PoissonRatio>0.33</PoissonRatio>
<CompressiveYieldStrength_MPa>480</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>503</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.11</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.875</HeatCapacity_JdgK>
<HeatConductivity_WdmK>130</HeatConductivity_WdmK>
<Density_gdcm3>2.81</Density_gdcm3>
<FusionLatentHeat_Jdg>390</FusionLatentHeat_Jdg>
<MeltingTemperature_C>635</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/Al6061T6.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>Al6061T6</Name>
<ElasticModulus_GPa>68.9</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>386</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>276</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.14</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.896</HeatCapacity_JdgK>
<HeatConductivity_WdmK>167</HeatConductivity_WdmK>
<Density_gdcm3>2.7</Density_gdcm3>
<PoissonRatio>0.33</PoissonRatio>
<FusionLatentHeat_Jdg>390</FusionLatentHeat_Jdg>
<MeltingTemperature_C>620</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/FC30.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>FC30</Name>
<ElasticModulus_GPa>110</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>900</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>200</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.01</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.46</HeatCapacity_JdgK>
<HeatConductivity_WdmK>52</HeatConductivity_WdmK>
<Density_gdcm3>7.2</Density_gdcm3>
<PoissonRatio>0.26</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1150</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/FDAC.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>FDAC</Name>
<CompressiveYieldStrength_MPa>1060</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>1240</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.11</ElogationRaioAtBreak>
<ElasticModulus_GPa>200</ElasticModulus_GPa>
<HeatCapacity_JdgK>0.5</HeatCapacity_JdgK>
<HeatConductivity_WdmK>33</HeatConductivity_WdmK>
<Density_gdcm3>7.85</Density_gdcm3>
<PoissonRatio>0.28</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1440</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/Inconel718.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>Inconel718</Name>
<CompressiveYieldStrength_MPa>1100</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>1100</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.25</ElogationRaioAtBreak>
<ElasticModulus_GPa>208</ElasticModulus_GPa>
<PoissonRatio>0.29</PoissonRatio>
<HeatCapacity_JdgK>0.435</HeatCapacity_JdgK>
<HeatConductivity_WdmK>11.4</HeatConductivity_WdmK>
<Density_gdcm3>8.19</Density_gdcm3>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1260</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/P20.WorkpieceMaterial
+14
View File
@@ -0,0 +1,14 @@
<WorkpieceMaterial>
<Name>Mold Steel P20</Name>
<Note>chatGPT review by mei</Note>
<ElasticModulus_GPa>205</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>860</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>720</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.1</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.46</HeatCapacity_JdgK>
<HeatConductivity_WdmK>29</HeatConductivity_WdmK>
<Density_gdcm3>7.85</Density_gdcm3>
<PoissonRatio>0.28</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1420</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/S440C.WorkpieceMaterial
+15
View File
@@ -0,0 +1,15 @@
<?xml version="1.0" encoding="utf-8"?>
<WorkpieceMaterial>
<Name>S440C</Name>
<Note>EN-X90CrMoV18; AISI-440C; UNS-S44004; JIS-SUS440C; DIN-1.4125; GB-9Cr18Mo; BS-BSEN10088-1 X90CrMoV18; AFNOR-Z100CD17; SS-2310</Note>
<ElasticModulus_GPa>210</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>2050</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>1950</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.02</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.46</HeatCapacity_JdgK>
<HeatConductivity_WdmK>24</HeatConductivity_WdmK>
<Density_gdcm3>7.7</Density_gdcm3>
<PoissonRatio>0.27</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1480</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/S45C.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>S45C</Name>
<ElasticModulus_GPa>190</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>450</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>490</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.17</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.4326</HeatCapacity_JdgK>
<HeatConductivity_WdmK>49.8</HeatConductivity_WdmK>
<Density_gdcm3>7.7</Density_gdcm3>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1440</MeltingTemperature_C>
<PoissonRatio>0.28</PoissonRatio>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/S50C.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>S50C</Name>
<ElasticModulus_GPa>205</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>580</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>540</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.16</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.49</HeatCapacity_JdgK>
<HeatConductivity_WdmK>50</HeatConductivity_WdmK>
<Density_gdcm3>7.85</Density_gdcm3>
<PoissonRatio>0.28</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1495</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/SCM440.WorkpieceMaterial
+14
View File
@@ -0,0 +1,14 @@
<WorkpieceMaterial>
<Name>SCM440</Name>
<Note>EN-42CrMoS4; EN-42CrMo4; ISO-42CrMo4; AISI-4140; JIS-SCM440; DIN-42CrMo4; GB-42CrMo; AFNOR-42CD4; AFNOR-42CD4u; UNI-42CrMo4; UNE-40CrMo41; UNE-40CrMo4; UNE-F1252; SS-2244; SFS-42CrMo4; GOST-35KHM; GOST-38KHM; BS-708M40; BS-CFS11</Note>
<ElasticModulus_GPa>210</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>950</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>785</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.15</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.46</HeatCapacity_JdgK>
<HeatConductivity_WdmK>42</HeatConductivity_WdmK>
<Density_gdcm3>7.85</Density_gdcm3>
<PoissonRatio>0.28</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1420</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/SS400.WorkpieceMaterial
+14
View File
@@ -0,0 +1,14 @@
<WorkpieceMaterial>
<Name>SS400</Name>
<ElasticModulus_GPa>200</ElasticModulus_GPa>
<PoissonRatio>0.26</PoissonRatio>
<CompressiveYieldStrength_MPa>245</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>245</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.2</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.49</HeatCapacity_JdgK>
<HeatConductivity_WdmK>50</HeatConductivity_WdmK>
<Density_gdcm3>7.85</Density_gdcm3>
<PoissonRatio>0.28</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1510</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/SUS304.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>SUS304</Name>
<CompressiveYieldStrength_MPa>215</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>215</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.7</ElogationRaioAtBreak>
<ElasticModulus_GPa>200</ElasticModulus_GPa>
<HeatCapacity_JdgK>0.5</HeatCapacity_JdgK>
<HeatConductivity_WdmK>16.2</HeatConductivity_WdmK>
<Density_gdcm3>8.0</Density_gdcm3>
<PoissonRatio>0.29</PoissonRatio>
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1440</MeltingTemperature_C>
</WorkpieceMaterial>
App/Resource/WorkpieceMaterial/Ti6Al4V.WorkpieceMaterial
+13
View File
@@ -0,0 +1,13 @@
<WorkpieceMaterial>
<Name>Ti6Al4V</Name>
<ElasticModulus_GPa>114</ElasticModulus_GPa>
<CompressiveYieldStrength_MPa>970</CompressiveYieldStrength_MPa>
<TensileYieldStrength_MPa>880</TensileYieldStrength_MPa>
<ElogationRaioAtBreak>0.14</ElogationRaioAtBreak>
<HeatCapacity_JdgK>0.5263</HeatCapacity_JdgK>
<HeatConductivity_WdmK>6.7</HeatConductivity_WdmK>
<Density_gdcm3>4.43</Density_gdcm3>
<PoissonRatio>0.34</PoissonRatio>
<FusionLatentHeat_Jdg>370</FusionLatentHeat_Jdg>
<MeltingTemperature_C>1604</MeltingTemperature_C>
</WorkpieceMaterial>