Seven new .mp fits from the fine/test sweeps (0.0001 .. 0.3), the S50C workpiece material and CuttingParameter side-files they reference, the schema-migrated S50C.hincproj, and the test-err-ratio project. These were produced by runs on HiNC-1 and existed only in dt's working tree. Co-Authored-By: Claude Opus 5 <noreply@anthropic.com>
15 lines
618 B
XML
15 lines
618 B
XML
<?xml version="1.0" encoding="utf-8"?>
|
|
<WorkpieceMaterial>
|
|
<Name>S50C</Name>
|
|
<Note></Note>
|
|
<ElasticModulus_GPa>205</ElasticModulus_GPa>
|
|
<PoissonRatio>0.28</PoissonRatio>
|
|
<CompressiveYieldStrength_MPa>580</CompressiveYieldStrength_MPa>
|
|
<TensileYieldStrength_MPa>540</TensileYieldStrength_MPa>
|
|
<ElogationRaioAtBreak>0.16</ElogationRaioAtBreak>
|
|
<HeatCapacity_JdgK>0.49</HeatCapacity_JdgK>
|
|
<HeatConductivity_WdmK>50</HeatConductivity_WdmK>
|
|
<Density_gdcm3>7.85</Density_gdcm3>
|
|
<FusionLatentHeat_Jdg>270</FusionLatentHeat_Jdg>
|
|
<MeltingTemperature_C>1495</MeltingTemperature_C>
|
|
</WorkpieceMaterial> |